Capilene® E 50 E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bocsOs_Capilene-E-50-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE® E 50 E is a low melt flow rate polypropylene homopolymer intended for extrusion, thermoforming and blow molding. CAPILENE® E 50 E features: easy processability, good melt stability, good mechanical properties. CAPILENE ® E 50 E is suitable for: in-line and off-line extrusion-thermoforming process for the production of cups and containers; extrusion of foils, sheets, strapping, slit film yarn, ropes and nets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 31.0 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 14 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1400 | MPa | ASTM D790 |
| -- 3 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 82.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525 4 |
| -- | 155 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF13WT6608 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Bayblend® FR3008 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Globalene® 6524 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| KOCETAL® K300EWBBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| TOLEN H038 TF/2 | SIBUR | PP Homopolymer | TOLEN |