Westlake LLDPE LF1020
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bnwWPF_Westlake-LLDPE-LF1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF1020 is a butene LLDPE with excellent mechanical and downgauging advantages. It is suitable for can liners, stretch wrap, agricultural film, and blending with LDPE. This product is available with various slip and antiblock formulations. Application/Uses: Stretch wrap Agricultural films Trash bags Co-extruded structures |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 186 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 207 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 10.3 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 10.3 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 35.9 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 24.8 | MPa | ASTM D882 |
| Dart Drop Impact 3(25 µm, Blown Film) | 120 | g | ASTM D1709A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 HF TFE 15 | RTP Company | PEI | RTP |
| Mirakutoran® TPU E580 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Moplen RP248R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| DeWAL DW 405 BNC | DeWAL Industries | UHMWPE | DeWAL |
| Rotuba CAP CP808 (13% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |