Latiohm 73/23-10 CNT
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiohm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bmboHv_Latiohm-73-23-10-CNT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Partially conductive/dissipative compound based on Polyoximethylene (POM). Carbon nanotubes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.1 to 2.3 | % | |
| Flow : 2.00 mm | 2.0 to 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 CF 20 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| TECHNO MUH LG5534 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Fainplast PVC GS 6612 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KOPLA PA66 KDP1100 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LEXAN™ LUX9616G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |