GLS Nylon 66 LK39
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bmB63V_GLS-Nylon-66-LK39.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon66 15% PTFE Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 to 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 2800 | MPa | ASTM D638 |
| Tensile Strength 1(Yield) | > 66.0 | MPa | ASTM D638 |
| Flexural Modulus | > 2400 | MPa | ASTM D790 |
| Flexural Strength | > 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 to 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 275 to 298 | °C | |
| Mold Temperature | 67.0 to 106 | °C | |
| Injection Pressure | 68.0 to 128 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 126 | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC GS 54/AM | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Durethan® BKV 140 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Lupoy® GN5001RF | LG Chem Ltd. | PC+ABS | Lupoy® |
| MAJ'ECO GEP160MHA | AD majoris | Biodeg Polymers | MAJ'ECO |