LNP™ LUBRICOMP™ YL003C compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bkCL23_LNP-LUBRICOMP-YL003C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4030 CCS Product Reorder name: YL003C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.5 to 1.7 | % | ASTM D955 |
| Across Flow : 24 hr | 1.7 to 1.9 | % | ASTM D955 |
| Across Flow : 24 hr | 1.8 | % | ISO 294-4 |
| Flow : 24 hr | 1.6 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr 1 | 0.20 | % | ASTM D570 |
| Saturation, 23°C | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 280 | MPa | ASTM D638 |
| -- | 260 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 90 | % | ASTM D638 |
| Break | > 450 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 290 | MPa | ASTM D790 |
| -- | 280 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 19.0 | MPa | ASTM D790 |
| -- | 12.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 3 | 23 | kJ/m² | ISO 180/1U |
| 23°C 4 | 48 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 5 | 88.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 54.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 57.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.8E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Results measured at 48 hrs |
| 2 . | 50 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*3 |
| 5 . | 80*10*4 mm |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 4010/02 GF 20 | ROMIRA GmbH | ABS+Nylon | Romiloy® |
| Sindustris POM N110LD | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Stat-Tech™ AS-15CF/000 BK001 | PolyOne Corporation | ABS | Stat-Tech™ |
| TRIREX® Compound VB3025G10 | Samyang Corporation | PC | TRIREX® Compound |
| Durez® 33163 | SBHPP | Phenolic | Durez® |