LNP™ LUBRICOMP™ DFL36 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | biHRRH_LNP-LUBRICOMP-DFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4036 Product reorder name: DFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Across Flow (24 hr) | 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9580 | MPa | ASTM D638 |
| -- | 9080 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 123 | MPa | ASTM D638 |
| Yield | 118 | MPa | ISO 527-2 |
| Break | 123 | MPa | ASTM D638 |
| Break | 118 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.6 | % | ASTM D638, ISO 527-2 |
| Break | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8620 | MPa | ASTM D790 |
| -- | 8340 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 186 | MPa | ASTM D790 |
| -- | 185 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.41 | ||
| Wear Factor - Washer | 22.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| 23°C 2 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 920 | J/m | ASTM D4812 |
| 23°C 3 | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 144 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® PA 5470/5 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| ULTEM™ 2310F resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| NEXUS PE LDPE-417 | Nexus Resin Group, LLC. | LDPE | NEXUS PE |
| OP - PC - Filled PC BK20 8SS | Oxford Polymers | PC | OP - PC - Filled |
| SHINSTRA AMG40TKB (PA66) | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |