Borealis PP EE189HPB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bhpBci_Borealis-PP-EE189HPB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EE189HPB is a 16% mineral filled polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1750 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 22.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 95 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 51.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN71120 | LyondellBasell Industries | LDPE | Microthene® G |
| Tarflen® SM-K25 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Terluran® HI-12 | INEOS Styrolution Group GmbH | ABS | Terluran® |
| Ducor® 1100 H | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| LNP™ THERMOCOMP™ IF006 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |