Generic PVOH
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bhO7PF_Generic-PVOH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PVOH This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.29 | g/cm³ | ISO 1183 |
| Solution Viscosity | 3 to 129 | mPa·s | ASTM D445 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 to 77 | µm | |
| Secant Modulus | |||
| MD | 8.96 to 20.4 | MPa | ASTM D882 |
| TD | 8.96 to 79.1 | MPa | ASTM D882 |
| 23°C | 8.96 to 23.0 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Break | 23.5 to 47.0 | MPa | ASTM D882 |
| 23°C | 24.2 to 77.9 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Break | 180 to 590 | % | ASTM D882 |
| Break, 23°C | 220 to 590 | % | ISO 527-3 |
| Dart Drop Impact (23°C) | 260 to 2200 | g | ASTM D1709, ISO 7765-1 |
| Elmendorf Tear Strength | |||
| MD | 90 to 1300 | g | ASTM D1922 |
| -- | 0.010 to 130 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 58.0 to 85.0 | °C | ISO 11357-2 |
| Melting Temperature | 180 to 230 | °C | ISO 11357-3 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1650 to 1660 | J/kg/°C | ASTM C351 |
| Thermal Conductivity (23°C) | 2.0 | W/m/K | ISO 8302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2000-75A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Anjatech® 250-E/UV/GF15 | Almaak International GmbH | Nylon 6 | Anjatech® |
| HiFill FR® PA6 GF20 FR HS L | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| OXNILON 66 ST-14GF | Oxford Polymers | Nylon 66 | OXNILON 66 |
| Pro-fax PL395N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |