Moplen EP440G
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgiHOI_Moplen-EP440G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen EP440G is a nucleated heterophasic copolymer especially developed for extrusion applications. Moplen EP440G exhibits high stiffness, very high impact properties at room and sub-zero temperatures, good dimensional stability and excellent creep and deforming resistance. The main applications of Moplen EP440G are thermoforming, corrugated board and extrusion blow moulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238, ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.80 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 48.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 29.4 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2 |
| Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 0°C | 9.0 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 190 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 78 | J/m | |
| 23°C | 740 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 78.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -55.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 66.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 65 | DIN 67530 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME B V2Y 15 SL5 | RIALTI Srl | PP, Unspecified | RIALFLAME |
| Prixene® EL200I25 | POLYMAT | LLDPE | Prixene® |
| DENKA STYROL MW-1-301 | Denka Company Limited | PS (GPPS) | DENKA STYROL |
| Fiberfil® J-60/10/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Sylvin 83048-85 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |