Tarnamid® T- 27 CF30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgav1u_Tarnamid-T--27-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is 30% carbon fibre reinforced polyamide 6 compound, heat stabilised, good conductive and electrostatic properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 255 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 15000 | MPa | ISO 178 |
| Flexural Stress 2 | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 9.3 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Rate | + | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | PA6, MHRZ, 14-190, CF30 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene 4440 (AS) | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| CERTENE™ LLMF-118D | Muehlstein | mLLDPE | CERTENE™ |
| ENSOFT SL-160-35D | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| E-RIALGLASS H 02 S 30 G | RIALTI Srl | PP Homopolymer | E-RIALGLASS |
| Lucent PA NP6-140 | Lucent Polymers, Inc. | Nylon 66 | Lucent PA |