RTV-2 P-44
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgIVGf_RTV-2-P-44.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| P-44 is a translucent, medium viscosity, high tear strength, platinum-catalyzed, RTV-2 silicone rubber, which was designed for casting parts where visual inspection is required. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show some inhibition sensitivity. P-44 is supplied with 2 Activators: P-44A (1) is used for production molds, while P-44A (2) is used for casting clear parts. P-44 is extremely useful for prototype applications where superior mechanical properties are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 316 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.925 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 11 | ||
| Resin | Mix Ratio by Volume: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 50000 to 60000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Clear/Transparent | ||
| -- 3 | Translucent | ||
| Viscosity | |||
| -- 4 | 1.0 to 2.0 | Pa·s | |
| -- 5 | 90 to 110 | Pa·s | |
| Curing Time | 16 to 24 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 38 to 46 | ||
| Shore A 7 | 38 to 46 | ||
| Tensile Strength | 3.79 to 4.48 | MPa | ASTM D412 |
| Tensile Elongation at Break | 230 to 280 | % | ASTM D412 |
| Tear Strength | 17.5 to 24.5 | kN/m | ASTM D624 |
| Electric Strength | 20 | kV/mm | |
| Relative Permittivity (100 Hz) | 2.90 | ||
| Volume Resistivity | 1.0E+15 | ohms·cm | |
| Dissipation Factor (100 Hz) | 3.0E-3 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | 7 Days |
| 7 . | 1 Day |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1935 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| XYRON™ VT31V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Fainplast PVC PH 75 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hifax TYC 852X E BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| Sumiliteresin® PR-55536 | SBHPP | Phenolic | Sumiliteresin® |