ALCUDIA® HDPE 5502E
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bfeHSl_ALCUDIA-HDPE-5502E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 5502E is a high-density polyethylene copolymer of hexene, with high molecular weight. It is specially designed to make, by blow molding-extrusion, tanks for liquid detergents and chemicals. This grade contains stabilizers according to the end use of the item in order to reinforce the thermal stability. Good environmental stress cracking resistance can be obtained with ALCUDIA® 5502E due to its molecular weight and density. TYPICAL APPLICATIONS Packaging of non-aggressive liquid detergents and chemicals. Recommended melt temperature range from 180 to 200°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.23 | g/10 min | |
| 190°C/21.6 kg | 22 | g/10 min | |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal) | 35.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 800 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 35F 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| EL-Lene™ H5615F | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| KRATON® D1118 B | Kraton Polymers LLC | SBC | KRATON® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 3105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Star T PA6 65E12 | Eurostar Engineering Plastics | Nylon 6 | Star T |