Durethan® BG 30 X 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bfVevY_DurethanBG30X000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers/glass spheres, injection molding, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.35 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.35 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.77 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.16 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.48 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.12 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 185 | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 6200 | 3500 | MPa | ASTM D638 |
| 23°C | 6300 | 3100 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 125 | 64.8 | MPa | ASTM D638 |
| Fracture, 23°C | 125 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 4.0 | 9.0 | % | ASTM D638 |
| Fracture, 23°C | 4.0 | 10 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 2400 | MPa | ISO 899-1 |
| 1000 hr | -- | 2000 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 5500 | 2800 | MPa | ASTM D790 |
| 23°C 6 | 5800 | 2800 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 195 | 110 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 170 | 80.0 | MPa | ISO 178/A |
| 23°C 7 | 185 | 100 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 8(23°C) | 5.0 | 8.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 14-060, (GB+GF) 30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 48 | 48 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 59 | 140 | J/m | ASTM D256 |
| -40°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 30 | 40 | kJ/m² | ISO 180/1U |
| 23°C | 35 | 60 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.70 | -- | J | ISO 6603-2 |
| 23°C | 2.00 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 690 | -- | N | ISO 6603-2 |
| 23°C | 700 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | 200 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | 180 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 10 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (1.50 mm) | 120 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 90.0 | -- | °C | UL 746 |
| RTI (1.50 mm) | 125 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.0E+16 | 1.0E+12 - 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+11 - 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 36 | 30 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 35 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 11 | 4.50 | 10.0 | IEC 60250 | |
| 23°C, 1 MHz 12 | 4.00 | 5.00 | IEC 60250 | |
| 23°C, 100 Hz | 4.50 | 16.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 4.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.015 | 0.20 | IEC 60250 | |
| 23°C, 100 Hz | 0.013 | 0.31 | IEC 60250 | |
| 23°C, 1 MHz | 0.020 0.018 | 0.060 0.10 | IEC 60250 | |
| Arc Resistance 13 | -- | 110 | sec | ASTM D495 |
| Comparative Tracking Index | ||||
| Solution a | 400 | -- | V | IEC 60112 |
| -- | -- | 450 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 14 | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | US-FMVSS302 |
| 10 . | 10°C/min |
| 11 . | Tinfoil Electrodes |
| 12 . | Tinfoil Electrodes |
| 13 . | Tungsten Electrodes |
| 14 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® AL2647 | Covestro - Polycarbonates | PC | Makrolon® |
| Bergamid™ B70 G10 H BK702 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| APEX® 2085-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Hostalen CRP 100 black | LyondellBasell Industries | HDPE | Hostalen |
| Sylvin 2900-60 White 1517 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |