SEALUTION™ 140 Peel Polymer
| Category: | POP , Peel Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | SEALUTION™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bfAD28_SEALUTION-140-Peel-Polymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEALUTION™140 easy-to-peel polymer is a peelable heat seal material that can form a peelable heat seal with the same material, polypropylene and polyethylene. Its formula has the characteristics of low COF and excellent thermal adhesive strength, which is helpful to improve the packaging processing performance. key characteristics: small granular blow molding and casting film can form peelable heat seal with the same material, polypropylene and polyethylene high thermal adhesive strength low COF formula slip agent: 6000 ppm opening agent: 9000 ppm processing aid: yes meets the following requirements: • EU, No 10/2011 • U.S. Food and Drug Administration • Please check the specific regulations for details |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 3.8 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 8.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Seal Initiation Temperature 1(51 µm, Blown Film) | 95.0 | °C | Internal method |
| Peelable range 2 | 95 - 130 | °C | Internal method |
| Extrusion instructions |
|---|
| Film thickness: 50 microns (2 mil) Coextruded blown film: A / B Coex, 80% / 20% layer ratio A = HDPE (40 µm / 1.6 mil) B = SEALUTION 140 (10 µm / 0.4 mil) Fabrication Conditions: Die Gap: 1.2 mm Melt Temperature: 180 - 230°C Blow-Up Ratio: 2.5 |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 1 psig (2.5 N/15mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (254 mm/s). |
| 2 . | Peelable range of 1-2 lb/in (2.5 - 5 N/15 mm) for this particular structure.Heat Seal Strengths, Topwave HT Tester 0.5 s dwell, 40 psi (2.76 bar) pressure, pull speed 10 in./min (254 mm/sec). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/HI | A. Schulman Europe | ABS | POLYMAN® |
| Sinvicomp SBF5758 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| DOW™ LDPE 421E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Karina BLACK PVC COMPOUND 70900-48/1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® NSB 90 BK-2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |