POCAN® DP C 1502 000000
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bf2UgT_POCANDPC1502000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilized |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm | 1.2 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm | 1.2 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.8 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 40 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2100 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 65.0 | MPa | ISO 178/A |
| 23°C 3 | 75.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 4(23°C) | 5.5 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+PC, GHLMPR, 11-020 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 19 | kJ/m² | ISO 179/1eA |
| 23°C | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 17 | kJ/m² | ISO 180/1A |
| 23°C | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B120 |
| Melting Temperature 5 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (4.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 265 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 70°C MT, 600 bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1000-GFR20 | QTR, Inc. | PC | QR Resin |
| Sindustris ABS LEF489 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Braskem PP RP 350 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Karina WHITE PVC COMPOUND 880-10/152-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DD0009E compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |