PLEXIGLAS® Sheet XT, UV transmitting Clear 0A770
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | PLEXIGLAS® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdkE1b_PLEXIGLAS-Sheet-XT-UV-transmitting-Clear-0A770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLEXIGLAS® XT Clear 0A770, an extruded clear and highly UV-permeable acrylic (polymethyl methacrylate, PMMA), was specially developed as a cover material for sun bed canopies. This means that elements made from this material are used to cover lamps in the roof section of solaria, sun beds etc.; PLEXIGLAS® XT 0A770 is not designed for rests/supports or parts entering into contact with sun bed users. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption - 24 h, 23°C 1 | 30.0 | ISO 62 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | 70 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Rating | |||
| -- | Class 3 | BS 476 Part 7 | |
| -- | M4 | NF P 92501 | |
| -- | B2 | DIN 4102 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance | UV permeable as of 250 nm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Forming Temperature - Reverse | > 80 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1B/1 |
| Tensile Stress 2 | 72.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/1B/5 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179/1fU |
| Notched Izod Impact Strength | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ISO 306/B |
| CLTE - Flow (0 to 50°C) | 7.0E-5 | cm/cm/°C | DIN 53752-A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+13 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 92.0 | % | DIN 5036-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Method 1 |
| 2 . | Type 1B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 9-APF-LM/Curene3005/St100 | Anderson Development Company | PUR-Ester/TDI | Andur |
| HiFill® PP GF20 CC HF | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Petrothene® LP540200 | LyondellBasell Industries | HDPE Copolymer | Petrothene® |
| POFEX EP8004S125F | POLYROCKS CHEMICAL CO., LTD | XLPE | POFEX |
| 3M™ Dyneon™ Fluoroelastomer FE 5840Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |