Sarlink® TPE AB-2349DN
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdNSby_Sarlink-TPE-AB-2349DN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-2349DN is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The main features of TPE AB-2349DN are:
Sarlink®The typical application field of TPE AB-2349DN is: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 23°C, 48 hours | 1.4 | % | ISO 2577 |
| Flow direction : 23°C, 48 hours | 1.4 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.10 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 49 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C, 2.00 mm | 92.7 | MPa | ISO 527-2/1 |
| 85°C, 2.00 mm | 34.5 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/500 | ||
| Fracture, -35°C, 2.00mm | 22.6 | MPa | ISO 527-2/500 |
| Fracture, 23°C, 2.00mm | 11.5 | MPa | ISO 527-2/500 |
| Fracture, 85°C, 2.00mm | 5.17 | MPa | ISO 527-2/500 |
| 100% strain, -35 c, 2.00mm | 21.9 | MPa | ISO 527-2/500 |
| 100% strain, 23°C, 2.00mm | 11.5 | MPa | ISO 527-2/500 |
| 100% strain, 85°C, 2.00mm | 5.43 | MPa | ISO 527-2/500 |
| Tensile Strain | |||
| Fracture | 390 | % | ISO 527-2 |
| Fracture, -35°C, 2.00mm | 250 | % | ISO 527-2/500 |
| Fracture, 23°C, 2.00mm | 420 | % | ISO 527-2/500 |
| Flexural Modulus 1 | ISO 178 | ||
| 23°C | 293 | MPa | ISO 178 |
| 85°C | 111 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| -35°C | 130 | kN/m | ISO 34-1 |
| 23°C | 78 | kN/m | ISO 34-1 |
| 85°C 2 | 19 | kN/m | ISO 34-1 |
| 85°C 3 | 36 | kN/m | ISO 34-1 |
| 85°C 4 | 39 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Glass Transition Temperature | -55.0 | °C | DSC |
| Melting Temperature (DSC) | 162 | °C | ISO 3146 |
| Additional Information |
|---|
| 最大吸水率 (在23 °C的平衡状态空气中，50%相对温度 = 0.01%最大吸水率(在23 °C的水中)= 0.01%火灾水平蔓延速率 (FMVSS 302)(试样厚度：1.0毫米)= 0.079 厚度 // 2.1 英寸/分钟雾化(3小时 @ 100 °C，21 °C 冷却板)= 96 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 227 - 243 | °C | |
| Nozzle Temperature | 232 - 249 | °C | |
| Processing (Melt) Temp | 232 - 249 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Method A, Pant-Shaped Specimen |
| 3 . | Method B, right-angle specimen (without cut) |
| 4 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1867 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| TOYOBO Urethane E2090A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| BESTNYL SI00VI02BH14 | Triesa Plastics | Nylon 6 | BESTNYL |
| LNP™ KONDUIT™ PX10323 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ KONDUIT™ |
| OTECH TPE OTO7510EP1 - A/V Jacket | OTECH Corporation | TPE | OTECH TPE |