Marlex® 9708
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdHfwq_Marlex-9708.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® 9708 is a High Density Polyethylene material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Marlex® 9708 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | < 10.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 1580 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, Compression Molded | 66.0 | °C | |
| 1.8 MPa, Unannealed, Compression Molded | 49.0 | °C | |
| Brittleness Temperature | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G20 NTLA010 PC305 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Next ABS SX-02BK | Next Polymers Ltd. | ABS | Next ABS |
| KOPLA PA66 KDR1031 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| KumhoSunny PBT/ASA HBA5810G | Shanghai KumhoSunny Plastics Co., Ltd. | PBT+ASA | KumhoSunny PBT/ASA |
| LOTTMER HX-086AB | Lotte Chemical Corporation | TPE | LOTTMER |