Iupilon® CFH2020
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bd2cmP_Iupilon-CFH2020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® CFH2020 is a Polycarbonate (PC) material filled with 20% carbon fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® CFH2020: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 4.8 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 4.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Flow : 3.20 mm | 0.050 to 0.20 | % | |
| Water Absorption (Saturation, 23°C) | 0.090 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 141 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 12500 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 151 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 146 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 9.0E-6 | cm/cm/°C | |
| Transverse | 5.9E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIPET® 2500G45 | Samyang Corporation | PET | TRIPET® |
| Durez® 32245 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| KOCETAL® VT301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Pebax® MV 1074 SA 01 | Arkema | PEBA-Ether | Pebax® |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |