LNP™ THERMOCOMP™ CX05470 compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bcepTG_LNP-THERMOCOMP-CX05470-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound CF-1004 ZS Product reorder name: CX05470 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.40 | % | |
| Across Flow : 24 hr | 0.20 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7080 | MPa | ASTM D638 |
| -- | 6810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 51.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/5 |
| Break | 64.8 | MPa | ASTM D638 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.2 | % | ASTM D638 |
| Yield | 1.1 | % | ISO 527-2/5 |
| Break | 1.2 | % | ASTM D638 |
| Break 5 | 1.3 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6480 | MPa | ASTM D790 |
| -- | 6340 | MPa | ASTM D790 |
| -- 7 | 6320 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 85.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 90.3 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 89.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 36 | J/m | ASTM D256 |
| 23°C 10 | 3.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D4812 |
| 23°C 11 | 9.7 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.10 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 97.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 93.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 92.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1401 | RTP Company | PESU | RTP |
| APEX® 2555-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Chemlon® E-6 GF30 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Polidan® PNT 0856/35 | Solvay Specialty Polymers | XLPE | Polidan® |
| Sylvin 7833-60 Red 6205 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |