AKROMID® B3 GF 15 9 RM-M natural (3679)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbsgBd_AKROMID-B3-GF-15-9-RM-M-natural-3679-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 15 9 RM-M natural (3679) is a 15% glass fibre reinforced, process improved polyamide 6 with average stiffness and strength, limited moisture absorption and light inherent color. Applications are housings and other dimensional stable parts in the automotive and electronic industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 83.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 15 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 180 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6200 | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 190 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 7.0 | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 225 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V971 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| WPP PP JOSB26287 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| BJB Polyurethane TC-802 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| HiFill® PA4/6 M/GF20 HS | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| Plexiglas® Rnew® B522 | Altuglas International of Arkema Inc. | PLA+PMMA | Plexiglas® |