Shanghai Ofluorine PVDF PF-1

Category:	PVDF , Polyvinylidene Fluoride
Manufacturer:	Shanghai Ofluorine Chemical Technology Co., Ltd
Trademark:	Shanghai Ofluorine PVDF
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bbpNbm_Shanghai-Ofluorine-PVDF-PF-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PF-1 PVDF film be made by our company's patent (China patent no. 201110048732.4), it is the PVDF base nanocomposite, white color and opaque, with high mechanical strength, good thermal stability, low gas/liquids permeability, fire retardant, our PVDF film can effectively separate and absorb ultraviolet, completely sunlight degradation resistance, with excellent chemical resistance and outdoor weather durability. PF type PVDF film mainly used as surface substrate material in the solar back sheet of coating composite technology.

Message

PF-1 PVDF film be made by our company's patent (China patent no. 201110048732.4), it is the PVDF base nanocomposite, white color and opaque, with high mechanical strength, good thermal stability, low gas/liquids permeability, fire retardant, our PVDF film can effectively separate and absorb ultraviolet, completely sunlight degradation resistance, with excellent chemical resistance and outdoor weather durability.

PF type PVDF film mainly used as surface substrate material in the solar back sheet of coating composite technology.

General Information
Features	Flame Retardant Good Chemical Resistance Good Thermal Stability Good Weather Resistance High Strength Low Gas Permeability Low Liquid Permeability Sunlight Resistant
Appearance	Opaque White
Forms	Film

Physical	Nominal Value	Unit	Test Method
Density	1.81 to 1.85	g/cm³	ISO 1183
Shrinkage ¹	< 1.0	%	ISO 11501

Optical	Nominal Value	Unit
UV Transmittance	< 1.0	%

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	24 to 26	µm	ISO 4593
Tensile Strength			ASTM D882
MD : Yield	> 30.0	MPa
TD : Yield	> 30.0	MPa
Tensile Elongation			ASTM D882
MD : Break	> 100	%
TD : Break	> 50	%

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	> 110	kV/mm	ASTM D149

Note Message
1 .	150°C for 30 min

Resin Grade	Manufacturer	Category	Trademark
DINALON® A1S25 G15	Grupo Repol	Nylon 66	DINALON®
FERREX® GPP20CC66HB	Ferro Corporation	PP Homopolymer	FERREX®
Durez® 33830	Sumitomo Bakelite North America, Inc.	Phenolic	Durez®
Petrothene® L3035	LyondellBasell Industries	LDPE	Petrothene®
Sylvin 8399-60 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin