Devcon Wear Resistant Putty (WR-2)
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbn6F3_Devcon-Wear-Resistant-Putty-WR-2-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A ceramic-filled epoxy putty with a smooth, low-friction finish. Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Specific Volume | 0.502 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 121 | °C | |
| Wet | 54 | °C | |
| Tensile Shear Adhesion | 15.2 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.050 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5170 | MPa | ASTM D638 |
| Flexural Strength | 44.8 | MPa | ASTM D790 |
| Compressive Strength | 67.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.70 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | 6.30 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 9.0 Mixing ratio by capacity: 4.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 45 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PH042L | Premier Polymers, LLC. | PP Homopolymer | Premier |
| RTP 100 HI | RTP Company | PP, Unspecified | RTP |
| Xuchuan XCW-90BA-6B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Zytel® HTN FR52G20NH NC010 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Dynaprene® VE5064A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |