PRL ABS-G30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbfNGy_PRL-ABS-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL ABS-G30 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.10 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 8960 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 96.5 | MPa | |
| Break, 3.18 mm | 96.5 | MPa | |
| Tensile Elongation (Yield, 3.18 mm) | 1.5 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 8270 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 113 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 107 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 191 to 199 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 210 to 227 | °C | |
| Processing (Melt) Temp | 210 to 238 | °C | |
| Mold Temperature | 48.9 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MPE-FG5 | Modified Plastics, Inc. | PE, Unspecified | Modified Plastics |
| Sylvin 9454-90LG Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Xuchuan XCD-600 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Polifil® Nylon 730 | The Plastics Group | Nylon 6 | Polifil® Nylon |
| Sylvin 5170-85 Red 6222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |