ASTALAC™ ABS X17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbTMb2_ASTALAC-ABS-X17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS X17 is a high heat resistance grade of ABS and is designed for injection moulding applications requiring a balance of heat resistance, impact toughness, product rigidity and mouldability. Typical applications include automotive interior console assemblies, glove-box lids, door-liner armrest substrates, grilles and appliques. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS X17UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 4.0 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 44.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 35 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 73.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.20mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 95.0 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 215 - 235 | °C | |
| Middle Temperature | 225 - 245 | °C | |
| Front Temperature | 235 - 255 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6600/40 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| WPP PP PPH3MG3.5-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Elastollan庐 1185A10X | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| ISOTHANE® 1095A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| MACOMASS PP MM-PP HE 25 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |