3M™ Dyneon™ PTFE Compound TF 6105N
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ba3Qzt_3M-Dyneon-PTFE-Compound-TF-6105N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.18 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.81 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 67 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 15.5 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 300 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 60.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 128018 A | RTP Company | PC+Polyester | RTP |
| Fenochem T 5700 | Chemiplastica, Inc. | Phenolic | Fenochem |
| Hylon® N1000EL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OXNILON 66 4IMP | Oxford Polymers | Nylon 66 | OXNILON 66 |