Electrafil® PPS GF35 SS7 BK
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bZRvGL_Electrafil-PPS-GF35-SS7-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Electrafil® PPS GF35 SS7 BK is a Polyphenylene Sulfide (PPS) product filled with 35% glass fiber and 7.0% stainless steel fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 257 | °C | |
| 1.8 MPa, Unannealed | 260 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+7 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 316 to 343 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 316 to 332 | °C | |
| Processing (Melt) Temp | 324 to 338 | °C | |
| Mold Temperature | 129 to 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR Polypropylene AP7535-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Ducor® 1087 K | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| POLYFLAM® RIPP 2000 HI | A. Schulman Europe | PP Copolymer | POLYFLAM® |
| TABOREN® PH 41 G 30-095 | SILON s.r.o. | PP Homopolymer | TABOREN® |
| Starex BF-0950 | LOTTE ADVANCED MATERIALS CO., LTD. | MABS | Starex |