MAJORIS FFR020X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bZEhX8_MAJORIS-FFR020X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS FFR020X is a polypropylene product,. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1970 | MPa | ISO 527-2/1 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress | 48.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 84.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Ball Pressure Test (125°C) | Pass | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Holding pressure: 30 to 60% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 187 | RTP Company | PP Homopolymer | RTP |
| Trademark PE LLH08925 | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Vipel® F701-ABM-23 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| LEXAN™ PK2870 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| NORYL™ WCV063 resin | SABIC Innovative Plastics | PPE+SEBS+Polyolefin | NORYL™ |