HIFOR® LT74105
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXWcGv_HIFOR-LT74105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WESTLAKE Hifor Polyethylene LT74105 is a high strength linear low density polyethylene containing medium slip and medium anitblock. It is designed for blown film applications and is well suited for customers and industrial packaging markets which require impact and tear strength. Films produces using LT74105 exhibit low imperfections and facilitate production at thinner guages. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 220 | MPa | |
| 1% Secant, TD | 241 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 50.0 | MPa | |
| TD : Break | 39.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 750 | % | |
| TD : Break | 1000 | % | |
| Dart Drop Impact | 170 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 45 | ASTM D2457 | |
| Haze | 14 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 EM L | RTP Company | PC | RTP |
| Bayblend® FR3010 HF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| AKROMID® B3 GM 15/15 black (1830) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Kumho KHS RM 21 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho KHS |
| PENTAMID AHT GV30 H TF15 black | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |