VESTAMID® HTplus M1933
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXS8Ur_VESTAMID-HTplus-M1933.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAMID HTplus M1933 is a glass-fiber reinforced (30%), Heat-stabilized polyphthalamide compound (PPA) containing a halogen-free flame retardant. It is free of red phosphorus. Due to the halogen-free flame retardant VESTAMID HTplus M1933 is especially suitable for interior parts in aircrafts, railway vehicles and ships. This compound can be used for injection molding and is especially suitable for manufacturing parts subjected to high temperature. Parts made of VESTAMID HTplusM1933 can be used in reflow soldering process. VESTAMID HTplus M1933 is supplied as spherical pellets in polyethylene packaging. We recommend a processing temperature between 325°C and 335°C during the injection molding process. The mold temperature should be within a range of 140°C to 180°C, preferably 160°C. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus M1933, please follow the general recommendations for PPA in our information „Handling and Processing of VESTAMID HTplus." |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 80°C, 2.00 mm | 0.90 | % | |
| Flow : 80°C, 2.00 mm | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 3.0 | kJ/m² | |
| 23°C, Complete Break | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 26 | kJ/m² | |
| 23°C, Complete Break | 28 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 301 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 267 | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 to 315 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | ||
| -- 2 | 575 | V | |
| Solution A | < 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.800 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm, Passes) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| 2 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 D TFE 15 | RTP Company | PPS | RTP |
| RR Advantage R-COPP 12 | Resin Resource, Inc. | PP Random Copolymer | RR Advantage |
| ALCUDIA® EVA PA-440 | REPSOL | EVA | ALCUDIA® EVA |
| Europrene® BR HV80 | Versalis S.p.A. | Rubber | Europrene® |
| KOCETAL® GF703 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |