Kingfa HG-108
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bWph7G_Kingfa-HG-108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa HG-108 is a polypropylene material, which contains a 15% filler. This product is available in North America or Asia Pacific,. The main features of Kingfa HG-108 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.5 - 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 29 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1530 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 39.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 51 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm, injection molding | 70.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 15% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-757 | CHI MEI CORPORATION | ABS | POLYLAC® |
| SABIC® HDPE PCG80063 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Crastin® LW9030 BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Lupoy® SR3108L | LG Chem Ltd. | PC | Lupoy® |
| LNP™ THERMOTUF™ MF004AI compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOTUF™ |