Asrene®UF 1810 is a linear low density polyethylene product,. It is available in North America, Europe or Asia Pacific. Asrene®UF 1810 applications include movies, wrappers and coating applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.60 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 50.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 850 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 30.0 µm | 24.5 | kN/m | ASTM D1922 |
| TD : 30.0 µm | 196.1 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Clarity (30.0 µm, Blown Film) | 75.0 | ASTM D1746 | |
| Haze (30.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 1.5 to 3.5 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E785PNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SUPREME Specialty PS SP255 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Argothane® 18411 | Argotec LLC | TPU, Unspecified | Argothane® |
| Cellophane™ CelloPlus™ W (White) | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Sylvin 8366-88C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |