Starex TX-0510F
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bVr0Xl_StarexTX0510F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TX-0510F is a methyl methacrylate/ABS (MABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: containers. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.30 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 | % | ISO 2577 |
| Traffic : 3.20mm | 0.30 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 106 | ASTM D785 | |
| R scale | 106 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 42.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 34.0 | MPa | ASTM D638 |
| Fracture | 32.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 30 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 59.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| 23°C 10 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 88.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 71.0 | °C | ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | |||
| 3200 µm | 88.0 | % | ASTM D1003 |
| 3200 µm | 88.0 | % | ISO 13468 |
| Haze | |||
| 3200 µm | 3.0 | % | ASTM D1003 |
| 3200 µm | 3.0 | % | ISO 13468 |
| Yellowness Index (3.20 mm) | -1.4 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYLOPET® EMC310TU | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| barex® 210 Injection Grade | INEOS Barex | Nitrile Resin | barex® |
| Generic PSU | Generic | PSU | Generic |
| Kepital® F30-02 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Sumiliteresin® PR-103 I | SBHPP | Phenolic | Sumiliteresin® |