Hostalen GM 5010 T3 black
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bUMo6l_Hostalen-GM-5010-T3-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen GM 5010 T3 black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 80 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.957 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | |
| 190°C/5.0 kg | 0.43 | g/10 min | |
| FNCT (80°C) 1 | > 20.8 | day | ISO 16770 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus | DIN 19537-2 | ||
| -- 2 | 470 | MPa | |
| -- 3 | 300 | MPa | |
| -- 4 | 1000 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Elongation - TD | > 350 | % | EN 638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 30 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 8.00 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 | |
| Staudinger Index - Jg | 310 | cm³/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 22.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C, 4.00 mm | 600 | % | |
| Tensile Creep Modulus 5 | ISO 899-1 | ||
| 1 hr | 640 | MPa | |
| 1000 hr | 300 | MPa | |
| Flexural Stress (3.5% Strain) | 18.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 24 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 200 to 280 | °C | |
| Middle Temperature | 200 to 280 | °C | |
| Front Temperature | 200 to 280 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 4.0 MPa, 2% Arkopal N 100 |
| 2 . | 24 hr, 4 point loading method |
| 3 . | 2000 hr, 4 point loading method |
| 4 . | 1 min, 4 point loading method |
| 5 . | 2 MPa Test Stress |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Colorite 66 Series 6066 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| Gallonprene® GP520-6009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| G-PAEK™ 1400G | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Hostacom HBG H02 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 8729-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |