DOWLEX™ 2045G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bUDPA0_DOWLEX-2045G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOWLEX™ 2045G Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films . Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 5.31 | J | Internal method |
| Film Puncture Force | 62.3 | N | Internal method |
| Film Puncture Resistance | 26.1 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 118 | J/cm³ | ASTM D882 |
| TD | 129 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 237 | MPa | ASTM D882 |
| 2% secant, MD | 205 | MPa | ASTM D882 |
| 1% secant, TD | 275 | MPa | ASTM D882 |
| 2% secant, TD | 232 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.3 | MPa | ASTM D882 |
| TD : Yield | 11.9 | MPa | ASTM D882 |
| MD : Fracture | 47.4 | MPa | ASTM D882 |
| TD : Fracture | 40.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 600 | % | ASTM D882 |
| TD : Fracture | 740 | % | ASTM D882 |
| Dart Drop Impact | 220 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 370 | g | ASTM D1922 |
| TD | 630 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 119 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 60 | ASTM D2457 | |
| Haze | 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸；30:1 L/D 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度： 418°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：41 rpm 冷却线高度: 43 in. |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A121 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| SABIC® STAMAX 40YM241 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| SHIN-A SER-550 | SHIN-A T&C | Epoxy | SHIN-A |
| NORYL™ PN275F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Moplen RP2965 | LyondellBasell Industries | PP Random Copolymer | Moplen |