AKROMID® B3 2 S3 natural (4018)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bU3d8V_AKROMID-B3-2-S3-natural-4018-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 2 S3 natural (4018) is an unreinforced, UV-stabilised, dry impact resistant polyamide 6 with light inherent color Applications are engineering parts like fasteners, clips, plugs and caps. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.4 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.3 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.0 | -- | % | ISO 178 |
| Tensile Modulus | 2400 | 800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 60.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.0 | 22 | % | |
| Break | > 50 | > 100 | % | |
| Flexural Modulus 2 | 1700 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 80.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 20 | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 145 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALEX 01FN002 - 3725 | AD majoris | PC | MALEX |
| RTP 4607 HI | RTP Company | SPS | RTP |
| Radilon® BGV 40 Natural | Radici Plastics | Nylon 6 | Radilon® |
| Trexlink™ 6770 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Multiuse Leostomer® LE-3180N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |