INEOS PP 200-CA13
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bSwMTV_INEOS-PP-200-CA13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene Random Copolymer for Injection moulding Benefits & Features 200-CA13 is a specially modified highly transparent polypropylene random copolymer with medium melt flow intended for injection moulding and injection stretch blow moulding. 200-CA13 is specially formulated for high speed injection moulding and contains nucleating and mould release additives allowing high de-moulding temperature as well as reduced cooling time. Products moulded from 200-CA13 have excellent transparency, very good organoleptical properties, good balance of stiffness and impact strength in ambient temperature, low blooming and good de-moulding properties. Applications 200-CA13 is designed for transparent injection moulded houseware, closures and food packaging needing good impact strength and excellent organoleptic properties. 200-CA13 is also suitable for injection stretch blow moulding (ISBM). Examples of products successfully injection moulded from 200-CA13 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C, Injection Molded) | 28.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| 0°C, Injection Molded | 3.3 | kJ/m² | |
| 23°C, Injection Molded | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A50 |
| Peak Crystallization Temperature (DSC) | 119 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 1000 µm | 15 | % | |
| 2000 µm | 30 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina BLACK PVC COMPOUND CAK 751-48/1-TEC-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF009S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LOXIM 831 02T HB | LOXIM Industries Private Limited | PP Copolymer | LOXIM |
| Polyrocks EP8400S90V-1 | Polyrocks Chemical Co., Ltd | PE, Unspecified | Polyrocks |
| Techsil® TIM11123 (GB) | Techsil Limited | Silicone Rubber, RTV-1 | Techsil® |