POLYFORT® FPP 20 GFM HI HH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bSW63a_POLYFORT-FPP-20-GFM-HI-HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% milled glass fibre PP homopolymer, impact modified, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 3.50 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 81.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/1A/50 |
| Fracture | 54 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 121 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 182 HEC | RTP Company | PP, Unspecified | RTP |
| WPP PP PPH2TF2-White | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Fainplast PVC PM 80/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| TECACOMP® PA66 CF15 black 4058 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Sylvin 8215-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |