Stanyl® 46HF4550
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bSTKcT_Stanyl-46HF4550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® 46HF4550 is a Polyamide 46 (Nylon 46) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® 46HF4550 are:
Typical application of Stanyl® 46HF4550: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.62 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 16000 | 11000 | MPa | |
| 120°C | 11000 | -- | MPa | |
| 160°C | 10000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 250 | 170 | MPa | |
| Break, 120°C | 150 | -- | MPa | |
| Break, 160°C | 135 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.2 | 3.5 | % | |
| Break, 120°C | 3.5 | -- | % | |
| Break, 160°C | 3.5 | -- | % | |
| Flexural Modulus | 15000 | 11000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 15 | kJ/m² | |
| 23°C | 15 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 70 | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ||||
| Flow | 3.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Transverse | 4.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Transverse | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 300 to 315 | °C | |
| Front Temperature | 300 to 315 | °C | |
| Nozzle Temperature | 300 to 310 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH2500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Trilliant™ HC HC6010-8001 WT | PolyOne Corporation | Nylon 6 | Trilliant™ HC |
| Axiall PVC 9175 Blue 90 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Elvax® 3190A | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Petrothene® GA568200 | LyondellBasell Industries | LLDPE | Petrothene® |