Generic PPA - Glass Fiber, Long
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bSGAxo_Generic-PPA---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPA - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.63 - 1.67 | g/cm³ | ASTM D792 |
| 23°C | 1.63 - 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.075 - 0.20 | % | ASTM D955 |
| 23°C | 0.060 - 0.48 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 - 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 18000 - 19300 | MPa | ASTM D638 |
| 23°C | 18500 - 20300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 200 - 232 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.8 - 1.9 | % | ASTM D638 |
| Fracture, 23°C | 1.4 - 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 17200 - 18100 | MPa | ASTM D790 |
| 23°C | 16900 - 17800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 359 - 395 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 - 310 | J/m | ASTM D256 |
| 23°C | 38 - 42 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 790 - 1200 | J/m | ASTM D256 |
| 23°C | 70 - 78 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 259 - 282 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 271 - 275 | °C | ISO 75-2/A |
| CLTE - Flow | 1.2E-5 - 3.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 135 | °C | |
| Processing (Melt) Temp | 324 - 325 | °C | |
| Mold Temperature | 135 - 152 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPA - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 8345 | Covestro - Polycarbonates | PC | Makrolon® |
| Naturacell® General | Rotuba Extruders, Inc. | CA | Naturacell® |
| AKROMID® A3 GF 60 1 black (2395) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Diakon® ST25H7 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| GELAST GT70ISB | Guang Sung Plastics (GSPL) | SEBS | GELAST |