EOS PA 3200 GF
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EOS GmbH |
| Trademark: | EOS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bS4oaN_EOS-PA-3200-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA 3200 GF is a whitish, glass-filled polyamide 12 powder, which is characterised by an excellent stiffness in combination with good elongation at break. Laser-sintered parts made from PA 3200 GF possess excellent material properties:
A typical application for PA 3200 GF is the usage e.g. for final parts within the engine area of cars, for deep-drawing dies or any other application which requires particular stiffness, high heat distortion temperature and low abrasive wear. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 80 | ISO 868 | |
| Ball Indentation Hardness | 98.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2500 | MPa | ISO 527-2 |
| -- 2 | 3200 | MPa | ISO 527-2 |
| Tensile Stress | |||
| -- 3 | 47.0 | MPa | ISO 527-2 |
| -- 4 | 51.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Break 5 | 5.5 | % | ISO 527-2 |
| Break 6 | 9.0 | % | ISO 527-2 |
| Flexural Modulus 7(23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress 8 | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 5.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 11 | |||
| 0.45 MPa, Unannealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 179 | °C | ISO 306/A50 |
| -- | 166 | °C | ISO 306/B50 |
| Melting Temperature 12 | 176 | °C | ISO 11357 |
| Note Message | |
|---|---|
| 1 . | Z Direction |
| 2 . | X Direction |
| 3 . | Z Direction |
| 4 . | Y Direction |
| 5 . | Z Direction |
| 6 . | Y Direction |
| 7 . | X Direction |
| 8 . | X Direction |
| 9 . | X Direction |
| 10 . | X Direction |
| 11 . | X Direction |
| 12 . | 20°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast PEVE 001 | NaturePlast | HDPE | NaturePlast |
| Hylon® N2025L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina CLEAR PVC COMPOUND 80/275-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® B-8130R | TEIJIN LIMITED | PC | Panlite® |
| Polygen SG6R | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |