VITAMIDE® BB16BK6671
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bQXWbQ_VITAMIDE-BB16BK6671.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BB16BK6671 is a Polyamide 6 (Nylon 6) product filled with 30% glass bead. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 1.1 | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 11 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3600 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Break | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 197 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 88.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 218 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 14 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- 1 | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 8500 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Staramide RB008 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| TOPAS® 8007S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Sylvin 29168-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® ABS ECO 2017/500 GF17 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |