MACOMASS PP MM-PP HI 21 (20% Talc)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | MACOMASS Verkaufs AG |
| Trademark: | MACOMASS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bPCBHi_MACOMASS-PP-MM-PP-HI-21-20-Talc-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MACOMASS PP MM-PP HI 21 (20% Talc) is a polypropylene homopolymer (PP Homopoly) material containing 20% talc filler. This product is available in Europe,. The main characteristics of MACOMASS PP MM-PP HI 21 (20% Talc) are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 - 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 - 22 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 8.0 | % | ISO 527-2 |
| Flexural Modulus | > 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | > 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | > 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 62.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Glow Wire Ignition Temperature | |||
| 1.60 mm | 750 | °C | |
| 3.20 mm | 750 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ NN-20CF/000 HI2 BK | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| Abstron IPM3000 | Bhansali Engineering Polymers Limited | ABS+Acrylic | Abstron |
| ACCUTECH™ CP0437G20M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| GS Pla® AD92W | Mitsubishi Chemical Performance Polymers, Inc. | Biodeg Polymers | GS Pla® |
| POCAN® KU 2-7317 000000 | LANXESS GmbH | PBT | POCAN® |