Order Products : sales@su-jiao.com
Infino NH-1035
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bOwOS0_Infino-NH-1035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino NH-1035 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Break | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 88 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2500 | MPa | ASTM D790 |
| -- 3 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 88.0 | MPa | ASTM D790 |
| -- 5 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 55 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 640 | J/m | ASTM D256 |
| 23°C 7 | 54 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 120 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 107 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 116 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 127 | °C | ISO 306/B50 |
| -- | 129 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 to 2.70 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 110 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® ESd 225 | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| TECOLITE KM-350(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| DOMAMID® 66G30H | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| LNP™ STAT-KON™ LX00486C compound | SABIC Innovative Plastics | PEEK | LNP™ STAT-KON™ |
| Sylvin 9077-95LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |