SANREX S10G20
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | SANREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bOiiI7_SANREX-S10G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SANREX S10G20 is a Styrene Acrylonitrile (SAN) product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| M-Scale | 92 | ASTM D785 | |
| M-Scale | 91 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 125 | MPa | ASTM D638 |
| Yield | 118 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5980 | MPa | ASTM D790 |
| -- | 6230 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 154 | MPa | ASTM D790 |
| -- | 158 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.2 | kJ/m² | ISO 179 |
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 104 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1203-80D | RTP Company | TPU-Polyester | RTP |
| POLYLON IR 1500 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| Thermoset Plastics 210 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Daelim Po1y® PP-331TW | DAELIM INDUSTRIAL CO., LTD. | PP Random Copolymer | Daelim Po1y® |
| Huafon JF-W-D6070 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |