LNP™ LUBRICOMP™ WAL34 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bOg2Ze_LNPLUBRICOMPWAL34compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WAL34 is a compound based on Polybutylene Terephalate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound WAL-4034 Product reorder name: WAL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.4 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4480 | MPa | ASTM D638 |
| Tensile Strength (Break) | 57.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 4400 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.082 | ASTM D3702 Modified | |
| With Self-Static | 0.065 | ASTM D3702 Modified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 180 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2101 HF | RTP Company | PEI | RTP |
| SUPREME GPPS SC 201 EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Arak LLDPE HD5813EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| LUVOCOM® TPE-7711/GY | Lehmann & Voss & Co. | TPE | LUVOCOM® |
| PERLER® N09H3000B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |