Radilon® A RV350LW 100 NAT 4817
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bO6lCS_Radilon-A-RV350LW-100-NAT-4817.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 35% glass fiber reinforced injection moulding grade. Lubricated, heat stabilized. Natural colour. Suitable for parts requiring high stiffness, good mechanical resistance and excellent heat ageing properties retention. Typical material used for automotive under bonnet components. ISO 1043 : PA66-T GF35 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 5.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11300 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 200 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 10400 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 305 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adstif EA5075 | PolyMirae | PP Copolymer | Adstif |
| ExxonMobil™ LDPE LD 157CW Blown | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Latilub 62-06GR | LATI S.p.A. | Nylon 6 | Latilub |
| Karina GRAY PVC COMPOUND 830-18/361-IS-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® DP AKV 50 HR H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |