Lustran® ABS Guardian™ 732
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bNxmMd_Lustran-ABS-Guardian-732.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran Guardian ABS 732 is an extrusion grade resin designed for use in thermoformed refrigerator and freezer liner applications. It is suitable for use with 245fa PU foams. As with any product, use of Lustran Guardian ABS 732 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 22.8 | MPa | |
| Break, 23°C | 28.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 100 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C, 12.7 mm | 75 | J/m | |
| 23°C, 12.7 mm | 200 | J/m | |
| Instrumented Dart Impact | Internal Method | ||
| -18°C, Total Energy | 16.3 | J | |
| 23°C, Total Energy | 33.9 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 2(1.8 MPa, Annealed) | 87.8 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Temperature Index (1.52 mm) | 60 | °C | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Critical Strain Energy 3(23°C) | > 1.0 | % | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.02 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | White |
| 2 . | Annealed 2 hours at 176°F |
| 3 . | 50:50 CO/OA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1600 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| 3M™ Dyneon™ PTFE Compound TF 4103 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| BIPEX B0320FN | Ginar Technology Co., LTD. | PBT | BIPEX |
| CALP FR240-2 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| REV Materials 8008-003 | REV Materials | PP, Unspecified | REV Materials |