Medalist® MD-165
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bN0WxC_Medalist-MD-165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for medical and healthcare applications requiring hard rubber characteristics. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.2 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 87 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 4.48 | MPa | ASTM D412 |
| 200% strain | 5.38 | MPa | ASTM D412 |
| 300% strain | 6.76 | MPa | ASTM D412 |
| Tensile Strength (Break) | 17.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength | 69.2 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 18 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 149 - 171 | °C | |
| Middle Temperature | 182 - 204 | °C | |
| Front Temperature | 193 - 216 | °C | |
| Nozzle Temperature | 216 - 238 | °C | |
| Processing (Melt) Temp | 216 - 238 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 171 | °C | |
| Cylinder Zone 2 Temp. | 171 - 182 | °C | |
| Cylinder Zone 3 Temp. | 182 - 204 | °C | |
| Cylinder Zone 5 Temp. | 193 - 216 | °C | |
| Die Temperature | 204 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADMER™ NF498A | Mitsui Chemicals America, Inc. | PE, Unspecified | ADMER™ |
| Calprene® 710 | Dynasol Elastomers | SBS | Calprene® |
| Hostacom TKS736D | LyondellBasell Industries | TPO (POE) | Hostacom |
| Karina BLACK PVC COMPOUND 920D48/ 4-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DEL34 compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |