SCHULABLEND® (PA/PP) M/MO 7101 GF8
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bLPIRe_SCHULABLENDPAPPMMO7101GF8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 8% glass fibre reinforced PA6/PP blend with excellent chemical resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 7.00 | -- | cm³/10min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | 2600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 47.0 | 46.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 5.4 | 8.9 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 44 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 61 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 195 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 99.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 156 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 31 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.5 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.5 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.5 mm | 675 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 675 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D black EL | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| CYCOLAC™ MG38F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Ecoflex® Supersoft 00-30 | Smooth-On, Inc | Silicone | Ecoflex® Supersoft |
| Gravi-Tech™ GRV-NP-110-W-NAT | PolyOne Corporation | Nylon 12 | Gravi-Tech™ |
| Karina GRAY PVC COMPOUND 853-18/323-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |